… with very low hydrogen content. Suitable for heat treatment. Step cooling is possible. High reserve of toughness and crack resistance. …

… constructions that needs post weld heat treatment after welding and still offers excellent impact properties. Due to the seamless production …

… strength should be buffered with CroNi 29/9 HL or 4370 HL. Up to 3 times faster! (less current with more deposit) No slag losses compare …

… the latest technologie. Due to the manufacturing process and two times anealing during the drawing process at 580ºC the hydrogen content …

… resistance to galling. It has cavitation-erosion resistance ten times that of 304 stainless steel, E Dur 12 can be used to protect …

… deposit is capable of taking a high polish. Structure: Austenite with delta ferrite. This fluxcored wire offers higher productivity, higher …

… resistance to galling. It has cavitation-erosion resistance ten times that of 304 stainless steel, Dur 12 can be used to protect …

… Welding instructions: - Preheating for sections >6 mm from 150 till 300 ºC is recommended. Use the normal standard welding techniques. …

… 450°C and keep that also as interpass temperature. Slowly cooling down, for example in an oven. … 56-59 HRc hardfacing …

… constructions that needs post weld heat treatment after welding and still offers mechanical properties confirming 5Y46 class. Due to the …