- … Nickel Iron based filler metal for joint welding and claddings on cast Iron. Very wel … wetting characteristics and high resistance against porosity. The weld metal is corrosion and heat resistant. Very well suitable for welding …
- … properties and extreme low hydrogen content below HD 3 ml/100gr weld metal. The weldmetal is suitable for longer post weld heat treatments as applied in …
- … coefficient that makes the alloy excelent for gliding surfaces and metal to metal wear. … Mixer blades, cutters, hoppers, sand pumps, friction …
- … surfaces in non-lubricating conditions due to its resistance to metal-to-metal wear. … Dur 12 PTA Powder is typically used for cutting tools … plungers; and for hardfacing of engine valves, pinch rollers in the metal-processing industries, and rotor blade edges. … Powder PTA DUR 12 …
- … CEWELD® AA MCrMo1V is a metal cored wire wire with Excellent weld puddle manipulation. Low … production process the hydrogen content is below 3ml/100g weld metal even after long storage in unconditioned conditiond. Good gap …
- … better wetting properties compared to solid wires. Ductile weld metal quality and X-ray soundness with easy slag removal and ferrite … Excellent against pitting and stress corrosion. The PREN above 35 weldmetal offers outstanding resistance against pitting. … ISO 15608: …
- … temperatures (500-800°C) under long term creep conditions. This filler metal can also be used for welding 321/321H and 347/347H grades in high … by intergranular HAZ cracking is reduced by using more ductile weld metal rather than 347H. … ISO 15608: 8.1 Austenitic ≤ 19 % Cr , TÜV …
- … suitable for TIG welding, easy to handle, high plasticity of the weld metal. High quality alloyed copper wire. The weld metal is a Copper-Silver alloy. Sound, pore free deposits and high …
- … interpass temperature and post weld treatment as required for the base metal. Hydrogen content: < 3 ml / 100 g weld metal. … < 620 MPa ISO 15608: 2.2, 3.1 (360 < ReH ≤ 690 MPa ) …
- … is recommended at 150 - 350° C. depending on the thickness of the base metal. Similar base metals should be pre-heated at 300° C to 400° C. … 1.4016, 1.4511, …