… low heat input and the interpass temperature should be limited to max. 150 °C. … 1.4898, GX45NiCrNbSiTi45-35  Parralloy H46M, Centralloy ET45, …

… anodizing. Non-heat treatable. Thicker sections should be preheated (150°C) prior to welding. … AlMgSi 0, AlSiMg (A), AlSi 1 MgMn, …

… Scale resistance up to 1150ºC, crack and wear resistant, suitable for rebuilding wornout parts. …

… Non-heat treatable. Thicker sections should be preheated (150°C) prior to welding. … G-AlSi10Mg, G-AlSi11 G-AlSi12 (Cu), …

… Scale resistance up to 1150ºC, crack and wear resistant, suitable for rebuilding wornout parts. …

… is possible. High reserve of toughness and crack resistance. Flux FL 150 of FL 160 can be used in combination with this wire. … 2,25% Cr, 1% …

… covers a weight range of alloys. Thicker sections should be preheated (150°C) prior to welding. … Aluminium alloys: AlMg3, AlMg4, …

… be kept below 15 kJ/cm and interpass temperature between 100 and 150ºC. … Reh < 690 MPa Iso 15608: 2.2 u 3.2 ( 460 < Reh ≤ 690(700) MPa …

… is a high performance electrode with a thick coating and a recovery of 150%. For welding heavy machinery, body and wagon building as well as …

… resistant up to 950ºC. Interpass temperature should be kept below 150ºC.  … 1.4828, 1.4829, 1.4893, 1.4835, 1.4818, 1.4825, 1.4826, …