Alloy: Sn94Ag6 / Solidus: 221°C / Liquidus: 279°C / Deposit color: Silver / Shear Strength (copper lap joint): 10,600 PSI

CEWELD L-Ag55Sn F is a flux-coated brazing rod (F). It is a universal silver brazing alloy without Cadmium with low operating temperature and high mechanical properties. Due to the addition of Sn. this alloy will show a bright looking joint and is more capillary then the standard silver brazing alloys.

Alliage de laiton facile à utiliser pour le brasage avec un flux séparé ou en utilisant le Gasflux (flux transporté par la flamme), de bonnes propriétés mécaniques et une résistance élevée à la corrosion. En raison des composants Fe, Mn et Sn, ce type d'alliage est appelé "bronze à basse teneur en fumées". 
Flux/pâte : CEWELD Universal-Flux

Easy to use brass alloy for brazing

Easy to use brass alloy for brazing without separate flux, (flux cored rod) good mechanical properties and high corrosion resistance.
Flux/Paste: CEWELD Universal-Flux

Alliage de laiton Ni-brass à haute résistance et bonne fluidité contenant du Nickel pour plus de résistance et de capacité de raccordement pendant le brasage avec d'excellentes propriétés de reconstruction.
Flux/Paste: CEWELD Universal-Flux

High strength brass alloy containing Nickel for more strength and bridging capability during brazing. Due to the special flux coating this type is mostly used in maintenance and repair, the flux coated rod can be bended very well without loosing flux.

Universal brazing alloy containing phosphor for use without additional flux on copper to copper joints. Good flowing characteristics very easy to use with high mechanical properties. 
 

Universal brazing alloy containing phosphor for use without additional flux on copper to copper joints. Good flowing characteristics. Very easy to use with high mechanical properties. 

Phosphorus silver brazing alloy. Self pickling on copper with good fluidity. Strong joints with good gab bridging properties. 
Flux/Paste: CEWELD Super-Flux