FILEUR DUR 402 M
AA 410 has higher hardness
and is used in valve seats to obtain better galling resistance. Normally to obtain
adequate ductility, preheat and post-weld heat-treatment are required . AA 410 is a
martensitic stainless steel that is heat-treatable. It has a nominal weld metal composition
of 12% Chromium. These weld deposits are air-hardenable that can normally be
heat-treated after welding
1.4000, 1.4001, 1.4002, 1.4003, 1.4006, 1.4008, 1.4021, 1.4024,
X6Cr13, X6CrAl13, X10Cr13, X15Cr13, X20Cr13, G-X10Cr13
AISI 410, 420
![PA](/sites/default/images/kenblad/PA_on.png)
![PB](/sites/default/images/kenblad/PB_on.png)
![PC](/sites/default/images/kenblad/PC_on.png)
Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
---|---|---|---|---|
As Welded | 330 HB |