… is recommended at 150 - 350° C. depending on the thickness of the base metal. Similar base metals should be pre-heated at 300° C to 400° C. … 1.4016, 1.4511, …

… 10 times faster than overlay welding by SMAW. No dilution with the basemetal and a full high hardness in the total thickness of the plate. No excessive heat that effects the basemetal or cause loose in strength two times faster to apply compare to …

… Outstanding alloy against high impact combined with abrasion including metal into metal friction. The weld deposit of CEWELD E Dur 60 Kb is one of the …

… very stable, spatter free arcs. This wire deposits low carbon weld metal of about 23%Cr-13%Ni-2.3%Mo. Cladding on low alloyed steels,the weld metal already achieves approximately the composition of ASTM 316 in the …

… °C and the deposition rate is 20-30% higher than with comparable tube metal. It is easy to use and inexperienced welders will have no … matters. Use a larger tip than is generally recommended for same diameter mild steel. Use slight excess acetylene feather. The deposit is …

… Fully austenitic weld metal with high resistance against stress corrosion cracking and … Ni, Mo and Cu. Sufficient resistance against oxidizing acids. The weld metal is corrosion resistant in sea water. CEWELD® SA Alloy 825 is best …

… Due to the high resistance to cracking and excelent toughness, all weld metal requires no buffer layer except on materials considered critical. … and shock. The interpass temperature should be maximum 250ºC. The weld metal is machinable with carbide tip tools, hardening is possible. The maximum hardness is dependent on the base metal and is achieved already in the first layer.  … Conveyors and …

… alloy offers extreme resistance against abrasion by minerals, all weld metal requires no buffer layer except on materials considered critical … completely crack free in single and multilay overlay welding. The weld metal is only machinable by grinding. Due to the production method (seamless copper coated flux cored wire) this wire can be stored …

… CEWELD® NiCu30Mn is a Nickel - Copper weld metal and has properties similar to “Monel 400”. It has good strength … in many media, including sea water, salts and reducing acids. The weld metal is not age hardenable and when used to join Monel K-500 it has lower strength then the base metal. … 2.4360, 2.4375, NiCu30Fe, NiCu30Al, Monel alloy 400, R405, …

… Extremely crack resistant weld metal conditioned by the basic slag. Low spatter loss, easy slag … for joining high carbon steels and when welding critical mixed base metal combinations. Ideal metallurgical choice for repair welding and production as well as for …