Haynes 718
Special alloy with age hardenable deposit and similar mechanical properties as the base metal. Age hardened condition: 720ºC for 8 Hours, furnace Cool 55ºC/ hour to 620ºC, than Air Cool for 8 hours.
Cr-Ni-Nb-Mo alloy and 718, 706, and X-750 alloys.
EN W.Nr.: 2.4668 (NiCr19Fe19Nb5Mo3), 2.4669 (NiCr15Fe7TiAl).
ASTM: B637, 5589.
UNS: N07718, N09706, N07750.
Inconel 718(2.4668), 706 and X-750 (X750)
![PA](/sites/default/images/kenblad/PA_on.png)
![PB](/sites/default/images/kenblad/PB_on.png)
![PC](/sites/default/images/kenblad/PC_on.png)
![PD](/sites/default/images/kenblad/PD_on.png)
![PE](/sites/default/images/kenblad/PE_on.png)
![PF](/sites/default/images/kenblad/PF_on.png)
Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
---|---|---|---|---|
As Welded | 580 | 860 | 28 | HRc |
Special alloy with age hardenable deposit and similar mechanical properties as the base metal. Age hardened condition: 720ºC for 8 Hours, furnace Cool 55ºC/hour to 620ºC than Air Cool for 8 hours
Inconel 718(2.4668), 706 and X-750 (X750)
![PA](/sites/default/images/kenblad/PA_on.png)
![PB](/sites/default/images/kenblad/PB_on.png)
![PC](/sites/default/images/kenblad/PC_on.png)
![PD](/sites/default/images/kenblad/PD_on.png)
![PE](/sites/default/images/kenblad/PE_on.png)
![PF](/sites/default/images/kenblad/PF_on.png)
![PG](/sites/default/images/kenblad/PG_on.png)
Heat Treatment |
RP0,2 (MPa) |
Rm (MPa) |
A5 (%) |
Hardness |
---|---|---|---|---|
As Welded | 580 | 860 | 28 | HRc |