… CEWELD E 6010 is a cellulose coated all positional pipe welding electrode designed especially for vertical down root pass welding on …

… low spatter loss, easy slag removal and hydrogen content below 3 ml/100gr. even after long unconditioned storage. … CuNi, Reh ≤ 460MPa ISo …

… input should be kept below 15 kJ/cm and interpass temperature between 100 and 150ºC. … Reh < 690 MPa Iso 15608: 2.2 u 3.2 ( 460 < Reh ≤ … 1.8927, 1.8931, 1.8928, 1.8974,  1.7147, 1.7149, 1.8734 S620Q, S620QL, S690Q, S690QL, S620QL1-S690QL1, 20MnCr65, 28CrMn4-3 L480 - L550, X65, X80, …

… properties.  Yield strength < 600 MPa. Low hydrogen content  HD< 3 ml/100g even after long storage. … Typical for:  Reh ≤ 550 MPa  ISO 15608: …

… oxidation depend on cycle frequency. In no case shall a temperature of 1000°C be exceeded. This alloy can withstand relatively severe thermic … is superior to type 309L. … ISO 15608: 8.1  Austenit ≤ 19 % Cr , TÜV 1000: Gr. 21-30,  Type: 25% Cr, 22%Ni  1.4710, 1.4713, 1.4724, 1.4726, …

… erosion and corrosion in high temperature (900 °C) environments. This electrode can also perfectly be used for applications which are subject …

… structural steels with Rp0,2 > 500 MPa. Low hydrogen content HD < 3 ml/100g even after long storage. … Reh ≤ 500 MPa, ISO 15608: 1.3, 2.1, 2.3 …

… filler metal offers excelent weldabillity and is the strongest in the 1000 series of the pure aluminium grades. Heavy parts and thicker … 1070A, EN AW 1350, 1060, 1070, 1080, and 3003. … Al99,0 … A 5.10: ER1100 … 18273: S Al 1100 (Al99,0Cu) …

… to the seamless production process the hydrogen content is below 3ml/100g weld metal even after long storage in unconditioned condition. …

… CEWELD 4332-Ti is a rutile basic electrode for joining heat resistant CrNi-steels of the same kind and … steel to stainless steel. … ISO 15608: 8.1  Austenit ≤ 19 % Cr , TÜV 1000: Gr. 21-30,  23% Cr, 12%Ni Type 1.2780, 1.4541, 1.4550, 1.4710, …