… deposit is capable of taking a high polish. Structure: Austenite with delta ferrite. This fluxcored wire offers higher productivity, higher …

… The weld deposit is offers strain hardening properties from 250 till 450 HB … austenitic manganese steel, high impact loads, hammers, …

… will show no undercut !Preheating is normally done to slow down the cooling speed, in case you can not control the cooling speed it is better to keep the work peace at a low temperature …

… arc at very low amps. Preheating is normally done to slow down the cooling speed, in case you can not control the cooling speed it is better to keep the work peace at a low temperature …

… arc at very low amps. Preheating is normally done to slow down the cooling speed, in case you can not control the cooling speed it is better to keep the work peace at a low temperature …

… will show no undercut !Preheating is normally done to slow down the cooling speed, in case you can not control the cooling speed it is better to keep the work peace at a low temperature … … Grey Cast Iron, Malleable cast iron, EN 1561: EN-GJL-100 (GG10) till EN-GJL-350 (GG35), EN 1562: EN-GJMB-350 (GTS 35) till EN-GJMB-550 …

… high Tungsten content the wear resistance against abrasion is 4 till 8 times better in comparison with C-Cr alloys … Sinter plant …

… diluted base material. Preheating is normally done to slow down the cooling speed, in case you can not control the cooling speed it is better to keep the work peace at a low temperature …

… Metal zones (WM) due to titanium nitride (TiN) precipitation in the still liquid metal in these zones, thus avoiding the risk of brittleness, which may sometimes occur when very thick welds are made (> 3 mm of sheet metal to be …

… mechanical properties the heat input should be kept around 10 KJ/cm. Cooling time (T8/5) must be adjusted by travel speed and preheat … grain structural steels (low temp) to StE 960 (StE 1100 to 12 mm) to S960QL1 (S1100 to 12 mm) … SA 890 … 26304-A: S4Ni2CrMo …