… resist high impact load, high heat, thermal shock, hot corrosion, compression, abrasion, erosion and many other forms of attack. The weld …

… risk of braking out or chipping of. In case of sensitive base material preheating is recommended at 300-400°C. Old Hardfacing layers should be …

… Seamless flux-cored wires represent a remarkable innovation in the field of welding, particularly …

… Can be welded crack free by preheating approxiamately 450°C and keep that also as interpass … for example in an oven. … 56-59 HRc hardfacing alloy, Mixing peddles, Press screws, Kneading machine, screw conveyors, pumps etc. … OA 54 L … …

… compared to CMn steels and sees the alloy being used for boiler, pressure vessel and piping construction. Typical with FL 155 Flux or FL …

… extreme high strength with excellent ductility and good weldabillity. Preheat and interpass temperature > 200°C …  1.7218, 1.7225 25 CD4, 13 …

… of the pure aluminium grades. Heavy parts and thicker plates should be preheated (150°C), prior to welding. At the same time, it keeps the …

… μm FSSS Apparent density (ISO 3923-2) 5.2-5.8 g/cm³ Particle shape: preponderantly spherical Coating microhardness: 800-1300 HV0.3 Sales … 3.3): -45+22 μm (*other sizes on request) -38+15 μm -25+10 μm … Compressor shafts, pump seals, flap actuators, paper rolls, ball valves, …

… as permanent stress by heat influence, metal wear and high surface pressure  … 1.4317, 1.4313, 1.4407, 1.4414,    GX4CrNi13-4, …

… as most commercial copper grades. Thicker sections than 5 mm should be preheated up to approximately 500 °C. … Cladding steel, Grey cast iron, …