… Very good abrasion resistance in combination with impact even at higher temperatures up to 550ºC. To much layers should be avoided, preheat is necessary to avoid cracking. A buffer layer with OA 4370 or …

… This alloy offers excellent weldability when properly cleaned prior to welding. Heavy parts and thicker plates should be preheated (150°C), prior to welding The alloy shows good … 3.3315, 3.3535, 3.3206, 3.3541, EN AW 5005A, EN AW 5754, EN AW 6060, EN AC 51100, EN AW 5454, EN AW 5251,   … AlMg 3 … A 5.10: ER5754 …

… Excellent welding properties with easily controllable flow permits … in case off multi-layer welding. The weld metal will show no undercut !Preheating is normally done to slow down the cooling speed, in case you … EN-GJS-400-15, EN-GJS-400-18, EN-GJS-450-10, EN-GJS-500-7, EN-GJS-600-3, EN-GJS-700-2                                       G GG-40, G …

… Due to the high resistance to cracking and toughness, all weld metal requires no buffer layer. Suited for wear parts subject to heavy pressure, impact and shock. The interpass temperature should be maximum …

… -ULTIMET wires easily produces crack-free weld deposits (over-matching weld overlays, weld inlays, and … cobalt-based alloys, allowing multiple layer build-ups with no pre-heating needed. -ULTIMET wire produces deposits wich harden quickly …

… The basic offshore electrode according to the latest offshore requirements for sub zero temperatures down to -60°C. CTOD tested and suitable up to steel types with 460 MPa yield strength (such as S460), approved according to grade 5Y46 …

… CEWELD ER80S-D2 Tig is a copper coated welding wire for welding of high strength steels, used predominantly after stress relieving. May find its use for joining … P295GH, P355GH, 16Mo3, 18MnMo4-5, 20MnMoNi4-5, P275NH, P355NH, P460NH, P355QH, P460QH, P500QH, GS-17CrMo55, GS-22CrMo5, GS-22CrMoV32, …

… This alloy offers excelent weldabillity when properly cleaned prior to welding. Heavy parts and thicker plates should be preheated (150°C), prior to welding The alloy shows good … 3.3315, 3.3535, 3.3206, 3.3541, EN AW 5005A, EN AW 5754, EN AW 6060, EN AC 51100, EN AW 5454, EN AW 5251 … AlMg 3 Tig … A 5.10: ER5754 …

… CEWELD E FeNi 60 N has a few benefits compare to other “FeNi” types … current, non conductive coating and a powerful arc at very low amps. Preheating is normally done to slow down the cooling speed, in case you … EN-GJS-400-15, EN-GJS-400-18, EN-GJS-450-10, EN-GJS-500-7, EN-GJS-600-3, EN-GJS-700-2. GGG40, GGG45, GGG50, GGG60; GGG70, GGG80 … E FeNi …

… point and narrow freezing range. In addition, it has a higher silicon content than AlSi5, which provides increased fluidity and reduced … elevated temperatures. Non-heat treatable. Thicker sections should be preheated (150°C) prior to welding. … G-AlSi10Mg, G-AlSi11, G-AlSi12 …